Preparation and Structural Characterization of Water-Soluble O-Hydroxypropyl……

Water-soluble hydroxypropyl chitin (HPC) derivatives were prepared by the reaction of chitin with propylene oxide in homogeneous conditions using a dimethylacetamide/5% lithium chloride solvent system. The reaction conditions for a proper substitution of the hydroxypropyl group were an 80°C reaction temperature, 24-h reaction time, and 48-h aging time. 1H-NMR and 13C-cross-polarization/magic angle spinning NMR spectroscopy were used for determining the substitution value and reaction site of substitution. It was found that the substitution reaction occurred mainly at the C6OOHgroup in the chitin molecules and water-soluble chitin derivatives could
be obtained at a substitution value higher than 0.35, which is known as a critical substitution value. X-ray diffraction analysis and FTIR spectroscopy showed that the structural characteristics of HPCderivatives were dependent on the substitution value.
As the substitution value of the HPC derivative increased the a-chitin crystal structure changed to the water-soluble b-chitin form in higher substitution values. Differences in the interchenic hydrogen bonding, interplanar spacing of the crystal lattice plane, and crystallinity can explain the structural changes upon substitution. The thermal decomposition temperature was also related to the characteristics of the crystalline structure, depending on a critical substitution value.

游客，如果您要查看本帖隐藏内容请回复

                               
登录/注册后可看大图

该贴已经同步到 一蓑烟雨的微博

谢谢分享

北风 发表于 2011-11-10 08:42

                               
登录/注册后可看大图

谢谢分享

不客气

谢谢，急需

谢谢，急需

KW412109889 发表于 2012-3-4 13:42

                               
登录/注册后可看大图

谢谢，急需

做什么用？